Room temp for zinc-iron compound Phosphating-Metal surface treatment agent

企业概况 / Company Profile

Room temp for zinc-iron compound Phosphating

Room temperature for zinc - iron compound Phosphating

RF-LY103

一、用途 First, use

RF-LY103室温锌－铁复合磷化剂是当代国际上新一代环保节能型高新技术品种。 RF-LY103 room temperature zinc - iron compound phosphate agent is a new generation of contemporary international environmental energy-saving high-tech varieties. 适用于各种形状和材质的钢铁构件，如钢铁、船舶、汽车、摩托车、自行车、洗衣机、冰柜、电控柜、变压器、货架、钢制家具和办公设备、中央空调等的静电喷粉、喷漆和电泳涂装前的磷化处理。 Various shapes and materials for the steel components, such as steel, shipbuilding, automobiles, motorcycles, bicycles, washing machines, freezers, electric control cabinet, transformer, shelves, steel furniture and office equipment, central air conditioning and other electrostatic spray, before painting and electrophoretic coating phosphating treatment. 亦适用于钢铁构件的工序间防锈。 Also apply anti-rust steel structures between processes.

二、特性 Second, the characteristics

本品系低锌、无渣、快速、彩色复合微晶薄膜型磷化，具有经济实惠、处理成本特别低，处理时间短、结晶细密、孔隙少、耐蚀性强，室内存放3～4周不锈；附着力强（0级），与漆膜配套性好，漆膜平整光滑，可提高漆膜的抗弯曲、抗冲击性能，对前处理要求不苛刻，允许强酸强碱处理；不需表面调整，不需钝化处理；处理温度低（5℃～40℃），磷化工艺范围宽，槽液控制简便（只测PH值）；槽液抗污染、抗杂质的能力强，不容易出现故障等特点。 The strains of low zinc, no residue, fast, color composite phosphate ceramic thin film, with economic benefits, particularly low processing cost, processing time is short, fine crystal, pore less, corrosion resistance, indoor storage is not 3 to 4 weeks rust; adhesion (0), and the film supporting good, smooth film can improve the coating's resistance to bending, impact resistance, on the pre-treatment requirements are not demanding, allowing acid and alkali treatment; no surface adjustment, without passivation; processing low temperature (5 ℃ ~ 40 ℃), Phosphating wide range of bath control is simple (only for PH); Bath anti-pollution, anti-impurities strong, not prone to failure and so on.

三、技术指标 Third, technical indicators

外观：浅绿色透明液体 Appearance: light green transparent liquid

PH值：工作液PH2.3～4.0。 PH value: the working fluid PH2.3 ~ 4.0.

膜重：0.8～2.0g/m ² Film weight: 0.8 ~ 2.0g / m ²

四、使用方法 The use of methods

1、本品以1：20稀释成工作液，槽液控制PH值在2.3～4.0。 1, the goods to 1:20 diluted working solution, 2.3 bath control PH value to 4.0.

2、处理工艺 2, the treatment process

⑴、无锈件：脱脂－水洗－水洗－磷化（浸渍3～10min，喷淋2min）－水洗－水洗去离子水洗（电泳）－干燥－涂装。 ⑴, rust-free components: fat - washing - washing - phosphate (dip 3 ~ 10min, spray 2min) - washing - washing deionized water washing (electrophoresis) - dry - painting.

⑵、有锈件：脱脂－水洗－酸洗－水洗－中和－水洗－磷化（浸渍3～10min，喷淋2min）－水洗－水洗－去离子水洗（电泳）－干燥－涂装。 ⑵, a rust pieces: skim - washing - acid - wash - and in - washing - phosphate (dip 3 ~ 10min, spray 2min) - washing - washing - washing deionized (electrophoresis) - dry - painting.

五、包装与贮存 V., packaging and storage

本品用25、50、200kg塑桶装，贮存于阴凉、通风、干燥处。 The product is 25,50,200 kg plastic drum, stored in a cool, ventilated, dry place.

六、保质期本品保质期为壹年。 Sixth, the product shelf life is one year shelf life.